タイトル*平成22年度中間年報 水素製造・輸送・貯蔵システム等技術開発 水素製造機器要素技術に関する研究開発 水素分離型リフォーマーの高耐久化・低コスト化研究開発(2)
公開日2012/2/17
報告書年度2010 - 2010
委託先名日本特殊陶業株式会社
プロジェクト番号P08003
部署名新エネルギー部
和文要約和文要約等以下本編抜粋:1. 研究開発の内容及び成果等 触媒一体化モジュールの研究開発において、長時間耐久性試験に供する為のモジュールを製作する。モジュールの劣化要因の調査を行い、課題を抽出する。一方、Fe 系異物付着の対策の他、
必要な劣化要因対策を盛り込んだ改良型MOC の開発を行う。今年度実施した研究開発の内容及び成果は以下の通りである。
(1)MOC の耐久性向上の研究 (a)耐久試験用MOC の製作および性能向上の検討 今年度も前事業にて初期耐久性を確認したφ 10mm × 300mmL のチューブ状MOC (
Membrane on Catalyst)を長時間耐久試験用やバンドル用、小容量リフォーマー試験用として製作した。
英文要約Title:Development of Technologies for Hydrogen Production, Delivery, and Storage Systems. Development of Elemental Technologies for Hydrogen Production Components. Research and Development for Increase of Durability and Cost Reduction of Membrane Reformer (2) (FY2008 - FY2012) FY2010 Annual Report

Tubular type MOC (Membrane On Catalyst) modules were fabricated by extrude molding process for duration tests. The size of MOC module was 10 mm in outside diameter and 300 mm in length. Long-term reforming tests were conducted with the MOC modules. Test results showed that degradation of reforming performance was not observed, while the purity of hydrogen production gradually decreased. The reasons of increasing amounts of impurity were leakages from pin-holes of Pd-Ag membrane, delamination of the membrane and incomplete sealing of the joint part connecting a support to a metal pipe. The pin-holes were caused by reaction of palladium with iron particles in the reforming environment or by growing local voids in the membrane formed in a plating process. In advanced MOC modules fabricated by press-molding process, we succeeded in fabricating the leakage-free module. Pd-Ag plating process of the advanced MOC module was improved to prevent pin-holes generation and delamination of the membrane during operation. Additionally a glass seal technique was adapted to the joint part. Long-term reforming tests with the advanced MOC modules were conducted. As a result, the purity of hydrogen production was kept over 99.9988 vol. % for more than 1000 hours.